Gears
The material used for all gears on the Liberty engine was selected at the option of the manufacturer from the following standard S. A. E. steels, the composition of which are given in Table 12, TABLE 12.--COMPOSITION OF STEELS NOS. X-3,340 AND 6,1... Hardening
The forgings can be hardened by cooling in still air or quenching in oil or water from a temperature between 1,650 and 1,750 deg.F. The physical properties do not vary greatly when the carbon is within the range of composition given, or when the ... Hardening
Steel is hardened by quenching from above the upper critical. Apparently the quick cooling prevents the normal change back to definite and sizeable crystals of ferrite and cementite. Hardness is associated with this suppressed change. If the change ... Hardening Carbon Steel For Tools
For years the toolmaker had full sway in regard to make of steel wanted for shop tools, he generally made his own designs, hardened, tempered, ground and usually set up the machine where it was to be used and tested it. Most of us remember the to... Hardening High-speed Steel
In forging use coke for fuel in the forge. Heat steel slowly and thoroughly to a lemon heat. Do not forge at a lower heat. Do not let the steel cool below a bright cherry red while forging. After the tool is dressed, reheat to forging heat to remove... Hardening High-speed Steels
We will now take up the matter of hardening high-speed steels. The most ordinary tools used are for lathes and planers. The forging should be done at carbon-steel heat. Rough-grind while still hot and preheat to about carbon-steel hardening heat, th... Hardening Operation
Hardening a gear is accomplished as follows: The gear is taken from the furnace by the furnaceman and placed in the lower die, surrounding the centering jaws, as shown at H in Fig. 62 and C in Fig. 63. Air is then turned into the cylinder D, and th... Hardness Testing
The word hardness is used to express various properties of metals, and is measured in as many different ways. Scratch hardness is used by the geologist, who has constructed Moh's scale as follows: Talc has a hardness of 1 Rock Salt h... Heat Treatment Of Axles
Parts of this general type should be heat-treated to show the following minimum physical properties: Elastic limit, 115,000 lb. per square inch; elongation in 2 in., 16 per cent; reduction of area, 50 per cent; Brinell hardness, 277 to 321. The h... Heat Treatment Of Gear Blanks
This section is based on a paper read before the American Gear Manufacturers' Association at White Sulphur Springs, W. Va., Apr. 18, 1918. Great advancement has been made in the heat treating and hardening of gears. In this advancement the chemic... Heat Treatment Of Lathe Planer And Similar Tools
FIRE.--For these tools a good fire is one made of hard foundry coke, broken in small pieces, in an ordinary blacksmith forge with a few bricks laid over the top to form a hollow fire. The bricks should be thoroughly heated before tools are heated. H... Heat Treatment Of Milling Cutters Drills Reamers Etc
THE FIRE.--Gas and electric furnaces designed for high heats are now made for treating high-speed steels. We recommend them for treating all kinds of Blue Chip tools and particularly the above class. After tools reach a yellow heat in the forge fire... Heat Treatment Of Punches And Dies Shears Taps Etc
HEATING.--The degree to which tools of the above classes should be heated depends upon the shape, size and use for which they are intended. Generally, they should not be heated to quite as high a heat as lathe tools or milling cutters. They should h... Heat Treatment Of Steel
Heat treatment consists in heating and cooling metal at definite rates in order to change its physical condition. Many objects may be attained by correct heat treatment, but nothing much can be expected unless the man who directs the operations know... Heat-treating Department
The heat-treating department occupies an L-shaped building. The design is very practical, with the furnace and the floor on the same level so that there is no lifting of heavy pots. Fuel oil is used in all the furnaces and gives highly satisfactory...

Open Hearth Process Sulphur Sulphur Composition Of Transmission-gear Steel Non-shrinking Oil-hardening Steels Steel For Chisels And Punches Surface Carburizing Vanadium

Quenching The Work Temperature For Annealing Heat Treatment Of Punches And Dies Shears Taps Etc Annealing In Bone Hardening High-speed Steel Steel Before The 1850's Correction By Zero Adjustment The Penetration Of Carbon