Lathe And Planer Tools
TO FORGE.--Gently warm the steel to remove any chill is particularly desirable in the winter. Then heat slowly and carefully to a scaling heat, that is a lemon heat (1,800 deg.-2,000 deg.F.), and forge uniformly. Reheat the tool for further forging ...
Leeds And Northrup Optical Pyrometer
The principles of this very popular method of measuring temperature are sketched in Fig. 123. The instrument is light and portable, and can be sighted as easily as an opera glass. The telescope, which is held in the hand, weighs only 25 oz.;...
Liberty Motor Connecting Rods
The requirements for materials for the Liberty motor connecting rods are so severe that the methods of securing the desired qualities will be of value in other lines. The original specifications called for chrome-nickel but the losses due to the dif...
Machineability
Reheating for machine ability was done at 100 deg. less than the drawing temperature, but the time of soaking is more than double. After both drawing and reheating, the blanks were buried in lime where they remain, out of contact with the air, until...
Making Steel Balls
Steel balls are made from rods or coils according to size, stock less than 9/16-in. comes in coils. Stock 5/8-in. and larger comes in rods. Ball stock is designated in thousandths so that 5/8-in. rods are known as 0.625-in. stock. Steel for makin...
Manganese
MANGANESE is a metal much like iron. Its chemical symbol is Mn. It is somewhat more active than iron in many chemical changes--notably it has what is apparently a stronger attraction for oxygen and sulphur than has iron. Therefore the metal is used ...
Manganese
Manganese adds considerably to the tensile strength of steel, but this is dependent on the carbon content. High carbon materially adds to the brittleness, whereas low-carbon, pearlitic-manganese steels are very tough and ductile and are not at all b...
Molybdenum
Molybdenum steels have been made commercially for twenty-five years, but they have not been widely exploited until since the war. Very large resources of molybdenum have been developed in America, and the mining companies who are equipped to produce...
Mushet And Bessemer
That Mushet was "used" by Ebbw Vale against Bessemer is, perhaps, only an assumption; but that he was badly treated by Ebbw Vale is subject to no doubt. Mushet's business capacity was small but it is difficult to believe that he could have been so f...
Nickel
Nickel may be considered as the toughest among the non-rare alloys now used in steel manufacture. Originally nickel was added to give increased strength and toughness over that obtained with the ordinary rolled structural steel and little attempt wa...
Nickel-chromium
A combination of the characteristics of nickel and the characteristics of chromium, as described, should obviously give a very excellent steel as the nickel particularly affects the ferrite of the steel and the chromium the carbon. From this combina...
Non-shrinking Oil-hardening Steels
Certain steels have a very low rate of expansion and contraction in hardening and are very desirable for test plugs, gages, punches and dies, for milling cutters, taps, reamers, hard steel bushings and similar work. It is recommended that for for...
Oil-hardening Steel
Heat slowly and uniformly to 1,450 deg.F. and forge thoroughly. Do not under any circumstances attempt to harden at the forging heat. After cooling from forging reheat to about 1,450 deg.F. and cool slowly so as to remove forging strains. ...
Open Hearth Process
The open hearth furnace consists of a big brick room with a low arched roof. It is charged with pig iron and scrap through doors in the side walls. Through openings at one end of the furnace come hot air and gas, which burn in the furnace, prod...
Optical System And Electrical Circuit Of The Leeds & Northrup Optical Pyrometer
For extremely high temperature, the optical pyrometer is largely used. This is a comparative method. By means of the rheostat the current through the lamp is adjusted until the brightness of the filament is just equal to the brightness of the image ...
« Previous
Next »
Showing
91
to
105
of
177
results
1
2
3
4
5
6
7
8
9
10
11
12
Most Viewed
Open Hearth Process
Sulphur
Sulphur
Composition Of Transmission-gear Steel
Non-shrinking Oil-hardening Steels
Steel For Chisels And Punches
Surface Carburizing
Vanadium
Least Viewed
Quenching The Work
Temperature For Annealing
Heat Treatment Of Punches And Dies Shears Taps Etc
Annealing In Bone
Hardening High-speed Steel
Steel Before The 1850's
Correction By Zero Adjustment
The Penetration Of Carbon