Annealing Of Rifle Components At Springfield Armory





In general, all forgings of the components of the arms manufactured

at the Armory and all forgings for other ordnance establishments

are packed in charcoal, lime or suitable material and annealed

before being transferred from the forge shop.



Except in special cases, all annealing will be done in annealing

pots of appropriate size. One fire end of a thermo-couple is inserted

in the center of the annealing pot nearest the middle of the furnace



and another in the furnace outside of but near the annealing pots.



The temperatures used in annealing carbon steel components of the

various classes used at the Armory vary from 800 deg.C. To 880 deg.C. or

1,475 to 1,615 deg.F.



The fuel is shut off from the annealing furnace gradually as the

temperature of the pot approaches the prescribed annealing temperature

so as to prevent heating beyond that temperature.



The forgings of the rifle barrel and the pistol barrel are exceptions

to the above general rule. These forgings will be packed in lime

and allowed to cool slowly from the residual heat after forging.